* 943X-8G6A4064 * 基础创新塑料(南沙) 943X-8G6A4064
规格用途
| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.18 | g/cm3 | |
| 密度 | ISO1183 | 1.19 | g/cm3 | ||
| 熔流率（熔体流动速率）(300°C/1.2kg) | ASTMD1238 | 10 | g/10min | ||
| 溶化体积流率（MVR）(300°C/1.2kg) | ISO1133 | 9.00 | cm3/10min | ||
| 收缩率-流动(3.20mm) | InternalMethod | 0.40to0.80 | % | ||
| MoldingShrinkage-AcrossFlow(3.20mm) | InternalMethod | 0.40to0.80 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 0.35 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 0.15 | % | ||
| 机械性能 | 拉伸模量2 | ASTMD638 | 2100 | MPa | |
| 拉伸模量 | ISO527-2/1 | 2100 | MPa | ||
| 抗张强度3(屈服) | ASTMD638 | 58.0 | MPa | ||
| 拉伸应力(屈服) | ISO527-2/50 | 55.0 | MPa | ||
| 抗张强度3(断裂) | ASTMD638 | 60.0 | MPa | ||
| 拉伸应力(断裂) | ISO527-2/50 | 60.0 | MPa | ||
| 伸长率3(屈服) | ASTMD638 | 6.0 | % | ||
| 拉伸应变(屈服) | ISO527-2/50 | 6.0 | % | ||
| 伸长率4(断裂) | ASTMD638 | 130 | % | ||
| 拉伸应变(断裂) | ISO527-2/50 | 130 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 2060 | MPa | ||
| 弯曲模量5 | ISO178 | 2200 | MPa | ||
| FlexuralStress5,6 | ISO178 | 85.0 | MPa | ||
| 弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 89.0 | MPa | ||
| 冲击性能 | 简支梁缺口冲击强度7 | -30°C | ISO179/1eA | 60 | kJ/m2 |
| 23°C | ISO179/1eA | 75 | kJ/m2 | ||
| 简支梁无缺口冲击强度7 | -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | |||
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 650 | J/m | |
| 23°C | ASTMD256 | 800 | J/m | ||
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 50 | kJ/m2 | |
| 23°C | ISO180/1A | 70 | kJ/m2 | ||
| 无缺口伊佐德冲击强度8 | -30°C | ISO180/1U | NoBreak | ||
| 23°C | ISO180/1U | NoBreak | |||
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 50.0 | J | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 135 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 120 | °C | ||
| 维卡软化温度 | ASTMD15259 | 140 | °C | ||
| ISO306/B120 | 140 | °C | |||
| BallPressureTest(125°C) | IEC60695-10-2 | Pass | |||
| 线形热膨胀系数-流动(-40到40°C) | ASTME831 | 6.5E-5 | cm/cm/°C | ||
| 线形热膨胀系数-流动(23到80°C) | ISO11359-2 | 7.2E-5 | cm/cm/°C | ||
| 线形热膨胀系数-横向(-40到40°C) | ASTME831 | 6.5E-5 | cm/cm/°C | ||
| CLTE-Transverse(23to80°C) | ISO11359-2 | 7.7E-5 | cm/cm/°C | ||
| RTIElec | UL746 | 125 | °C | ||
| RTIImp | UL746 | 115 | °C | ||
| RTIStr | UL746 | 120 | °C | ||
| 电气性能 | DielectricStrength(3.20mm,inOil) | ASTMD149 | 17 | kV/mm | |
| 介电强度(3.20mm,在油中) | IEC60243-1 | 16 | kV/mm | ||
| 介电常数 | 50Hz | ASTMD150 | 2.95 | ||
| 60Hz | ASTMD150 | 2.95 | |||
| 1MHz | ASTMD150 | 2.90 | |||
| 耗散因数 | 50Hz | ASTMD150 | 2.4E-3 | ||
| 60Hz | ASTMD150 | 2.4E-3 | |||
| 1MHz | ASTMD150 | 8.5E-3 | |||
| 相比耐漏电起痕指数(CTI) | UL746 | PLC3 | |||
| 漏电起痕指数 | IEC60112 | 225 | V | ||
| 高电弧燃烧指数(HAI) | UL746 | PLC0 | |||
| 热丝引燃(HWI) | UL746 | PLC1 | |||
| 可燃性 | UL阻燃等级 | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | |||
| 灼热丝易燃指数(1.0mm) | IEC60695-2-12 | 960 | °C | ||
| 热灯丝点火温度(1.0mm) | IEC60695-2-13 | 825 | °C | ||
* 943X-8G6A4064 * 基础创新塑料(南沙) 943X-8G6A4064
...