透明电车头头盔面罩料
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 |
|
|
|
| -- 2 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 3 | 63.0 | MPa | ASTM D638 |
| 屈服 | 63.0 | MPa | ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服 4 | 6.0 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/50 |
| 断裂 5 | > 70 | % | ASTM D638 |
| 断裂 | > 70 | % | ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| 弯曲应力 |
|
|
|
| -- | 90.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 90.0 | MPa | ASTM D790 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 |
|
|
|
| R 级 | 120 |
| ASTM D785 |
| R 计秤 | 120 |
| ISO 2039-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 9 | 12 | kJ/m2 | ISO 180/1A |
| 23°C 10 | 70 | kJ/m2 | ISO 180/1A |
| 无缺口悬臂梁冲击 |
|
|
|
| 23°C | 无断裂 |
| ASTM D4812, ISO 180/1U |
| -30°C 11 | 无断裂 |
| ISO 180/1U |
| 装有测量仪表的落镖冲击 (23°C, Energy at Peak Load) | 65.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm | 138 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距 12 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 13 | 127 | °C | ISO 75-2/Af |
| 维卡软化温度 | 143 | °C | ISO 306/B50, ASTM D1525 14 |
| Ball Pressure Test (125°C) | Pass |
| IEC 60695-10-2 |
| 线形热膨胀系数 - 流动 |
|
|
|
| -40 到 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| 23 到 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| 导热系数 | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| 介电强度 (1.60 mm) | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| 介电常数 |
|
| ASTM D150, IEC 60250 |
| 60 Hz | 3.00 |
| ASTM D150, IEC 60250 |
| 1 MHz | 3.00 |
| ASTM D150, IEC 60250 |
| 耗散因数 |
|
| ASTM D150, IEC 60250 |
| 60 Hz | 1.0E-3 |
| ASTM D150, IEC 60250 |
| 1 MHz | 0.010 |
| ASTM D150, IEC 60250 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 (1.60 mm) | V-2 |
| UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 折射率 | 1.586 |
| ASTM D542, ISO 489 |
| 透射率 (2540 μm) | 88.0 到 90.0 | % | ASTM D1003 |
| 雾度 (2540 μm) | < 0.80 | % | ASTM D1003 |
LEXAN™ *1000R resin
聚碳酸酯
SABIC Innovative Plastics
产品说明：
*1000R resin is a medium-low flow (MFR = 10 at 300°C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. It is available exclusively at
LEXAN™ *1000R resin 物性表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 1.20 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 9.50 | cm3/10min | ISO 1133 |
| 收缩率 - 流动 |
|
| 内部方法 |
| -- 1 | 0.50 到 0.70 | % | 内部方法 |
| 3.20 mm | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 |
|
|
|
| 饱和, 23°C | 0.35 | % | ISO 62 |
| 平衡, 23°C | 0.35 | % | ASTM D570
|